Pupure, Liva; Varna, Janis; Joffe, Roberts; Berthold, Fredrik; Miettinen, Arttu

Composites formed from wood fibers and man-made cellulosic fibers in PLA (polylactic acid) matrix, manufactured using sheet forming technique and hot pressing, are studied. The composites have very low density (due to high porosity) and rather good elastic modulus and tensile strength. As expected, these properties for the four types of wood fiber composites studied here improve with increasing weight fraction of fibers, even if porosity is also increasing. On the contrary, for man-made cellulosic fiber composites with circular fiber cross-section, the increasing fiber weight fraction (accompanied by increasing void content) has detrimental effect on stiffness and strength. The differences in behavior are discussed attributing them to fiber/ fiber interaction in wood fiber composites which does not happen in man-made fiber composites, and by rather weak fiber/matrix interface for man-made fibers leading to macro-crack formation in large porosity regions.